March 2017

Make holes for TiC rods on the foam molds

03/31/2017 langfeng tic based cermet

Please soak TiC inserts into borax solution,then dry them before application(deoxidization process and secure the tight binding with TiC rods and hammer head) Weld iron nails on TiC rods. The main purpose of iron nail to fix position [Read More]

Synthesis of Reaction Technology under Microwave Atmospheric Pressure

03/24/2017 langfeng industry microwave furnace

Microwave technology used in atmospheric pressure organic synthesis reaction, select a long neck of the conical flask, placed in the conical flask reaction compound solvent, in the middle of the middle of the microwave punching, installed on the [Read More]

Microwave materials

03/16/2017 langfeng industry microwave furnace

The behavior of the material in the microwave field can be divided into three types: 1) Microwave Transparent Materials: Mainly low loss insulating material, which allows microwave reflection and partial transmission, but rarely absorbs microwave, such as most [Read More]

Chromium carbide powder professional introduction

03/10/2017 langfeng carbide powder

Chromium carbide powder: CAS No:12075-40-0, UN number: 3178, density:6.68g/cm3, melting point: 1890°C…etc, formula: Cr3C2,Cr7C3,Cr23C6,CrC. Chromium carbide powder has the properties of good corrsion resistance, wear resistance, oxidation resistance even under high temperature of 1000-1000 degress. Carbide chromium powder [Read More]

Carbide Metal powder for Hard Metal

03/02/2017 langfeng Uncategorized

Changsha Langfeng metallic Co don’t provide the Granulated Ready to Press Hard Metal Powder , but some of our metal carbide powder can be used for hard metal as additive materia, for example, ZrC, VC, TiC, TaNbC, Cr3C2 etc [Read More]

The best HRC is 60-63 of LFT12 TM52 Titanium based steel bonded carbide rod

03/01/2017 langfeng tic based cermet

The best HRC is 60-63 of LFT12 TM52 Titanium based steel bonded carbide rod, because of the work hardening phenomenon, the HRC of the TiC surface layer would be higher during impact can meet HRC 62-65 [Read More]